Explore the cracking problem of red sandalwood, huanghuali and red rosewood

Regarding the cracking of furniture, it is estimated that the most heard is the red rosewood crack, especially in the homes with heating in the north; the red sandalwood will appear cracks in the summer in the high temperature indoors or in the dry north wind in winter; yellow Pear (Vietname) is very good in the summer, no problem, in the winter under the northerly wind, there is a filament crack; red rosewood is also very good in the summer, no problem, in the dry north wind in winter, the crack is more powerful than the yellow pear.

Regarding the cracking of furniture, it is estimated that the most heard is the red rosewood crack, especially in the homes with heating in the north; the red sandalwood will appear cracks in the summer in the high temperature indoors or in the dry north wind in winter; yellow Pear (Vietname) is very good in the summer, no problem, in the winter under the northerly wind, there is a filament crack; red rosewood is also very good in the summer, no problem, in the dry north wind in winter, the crack is more powerful than the yellow pear.

It seems that the maintenance of winter mahogany for mahogany furniture is more important, but the furniture that is not cracked is probably only plastic, and the purple-yellow furniture of the author's family is also cracked, but less than the acid branch. However, if there is obvious crack on the surface of the furniture that has just been bought and whether the powder is normal, the relevant experts said: "It should be regarded as a normal phenomenon."

Think carefully, split into: fine cracks, wind cracks and cracks, fractures. Fine cracks and wind cracks are normal. Wind cracks and fine cracks are a natural taste of wood. After regular wax maintenance, wood can be self-filled and repaired by secretions. Cracking and breaking are natural unacceptable errors.

Finally, the author thinks that the waxing and painting are cracked, which is related to the humidity and the light source. When the wood is made and used, if the external conditions are different, I will analyze the material without any cracking. From the point of view, the internal stress of the hot and swollen wood shrinkage is always working. If the internal stress cannot be eliminated by plastic deformation, the material is not cracked. Which is the rush to the vent? Under the squat, the small crack is even younger. The acne!